Vacuum Bagging Release Film
DESCRIPTION
HG193 release film is an industrial used high temperature film for autoclave applications up to 193°C. It is not stickable to epoxy and phenolic resin systems. Both perforated release films and non-perforated release film can be chosen.
ADVANTAGES
• Can lower the production cost as the film is with reasonable price
• The film is flat and can be smoothened easily to prevent any wrinkles on the product surface when undergoing vacuum bagging
• Perforated and non-perforated can be chosen and the colour is sharp and visible
• Outstanding elongation at break which is good for autoclave
TECHNICAL DATA
|
Material type |
PMP |
|
Elongation at break |
250 % |
|
Tensile strength |
3400 psi (23 MPa) |
|
Maximum use temperature |
193°C |
|
Materials to avoid |
Polyester and vinyl ester resins |
|
Color |
Blue/Clear |
|
Shelf life |
Unlimited when stored in original packaging at 22°C |
SIZES
|
Thickness |
Width |
Forms Available |
|
38 μ m |
3.05 m |
Sheeting, Centrefold |
|
50 μ m |
1.37 m |
Centrefold |
NOTES
The maximum use temperature is dependent upon the duration at maximum temperature and is process specific, HG recommends testing prior to use.
Hot Tags: vacuum bagging release film, China vacuum bagging release film manufacturers, suppliers, factory, peel ply polyester, non perforated release film, Vacuum Bagging Film For Composites, peel ply fabric, release film composites, bagging film